7A04 T6 extruded aluminum round bar

7A04 T6 extruded aluminum round bar is an ultra-high-strength aluminum alloy of Al-Zn-Mg-Cu, also known as super-hard aluminum. It is a mature, super-hard aluminum alloy. It is a long-lasting and widely used alloy with high strength, good heat treatment strengthening effect, moderate plasticity under annealing and new quenching conditions; unlike hard aluminum, the corrosion resistance under artificial aging is better than that of natural aging, and the natural aging process is slow.It will take 3 month to reach the age hardening peak.so 7A04 T6 extruded aluminum round bar is used in the quenching artificial aging state. The disadvantage is that the stability of the structure is not high, the low-frequency fatigue strength is low, and there is a tendency of stress corrosion cracking. The alloy spot weld has good weldability, poor gas welding, good machinability after heat treatment, but poor machinability after annealing.

Composition of 7A04 T6 extruded aluminum round bar
 

Element	Si	Fe	Cu	Mn	Cr	Mg	Zn	Ti	Al
7A04	≤0.5	≤0.5	1.4-2.0	0.2-0.6	0.1-0.25	1.8-2.8	5.0-7.0	≤0.1	Rem

 
Mechanical properties of 7A04 T6 extruded aluminum round bar According to GB/T 3191-1998
 

加工方式 Processing	状态 Temper	直径mm Dia	抗拉强度Mpa Tensile Strength	屈服强度Mpa Yield Strength	伸长率 Elongation
Extruded	T6	22~150	≥530	≥400	≥6